Methods for preparing slurries of coated particulates

ABSTRACT

Methods of creating a stable slurry of coated particulates wherein the slurry is capable of being stored for at least 2 hours before use comprising the steps of: providing resin coated particulates wherein the resin comprises a resin that does not completely cure unless it is at least one of exposed to a temperature above about 175° F. or exposed to an external catalyst; and, substantially suspending the resin coated particulates in a servicing fluid to create a stable resin coated particulate slurry. Methods of creating a stable slurry of coated particulates wherein the slurry is capable of being stored for at least 2 hours before use comprising the steps of: providing tackifier coated particulates; and, substantially suspending the tackifier coated particulates in a servicing fluid to create a tackifier coated particulate slurry.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention involves coated proppant slurries and using such slurries in subterranean applications such as production enhancement and sand control. More particularly, the present invention relates to stable resin-coated proppant suspensions that need not be immediately used once they are formed.

2. Description of Related Art

Servicing fluids comprising particulates are used in a variety of operations performed on subterranean wells, such as production stimulation operations like fracturing and well completion operations like gravel packing. Often, it is desirable for such particulates to consolidate into a permeable pack or mass. One method of achieving such consolidation involves coating the particulates with a curable resin before they are used in a subterranean operation so that they consolidate once down hole.

One example of a production stimulation operation using a servicing fluid having particulates suspended therein is hydraulic fracturing, wherein a formation is treated to increase its permeability by hydraulically fracturing the formation to create or enhance one or more cracks or “fractures.” Such hydraulic fracturing is usually accomplished by injecting a viscous fracturing fluid into the subterranean formation at a rate and pressure sufficient to cause the formation to break down and produce one or more fractures or enhance one or more natural fractures. The fracture or fractures may be horizontal or vertical, with the latter usually predominating, and with the tendency toward vertical fractures increasing with the depth of the formation being fractured. The fracturing fluid is generally a highly viscous gel, emulsion, or foam that comprises a particulate material often referred to as proppant. In some fracturing operations, commonly known as “water fracturing” operations, the fracturing fluid viscosity is somewhat lowered, the proppant concentration is in the range of from about 0.5 to about 2 pounds per gallon, and the proppant remains in suspension because the fracturing fluid is injected into the formation at a substantially higher velocity. Whether a highly viscous fluid or a less viscous fluid with a higher velocity is used, proppant is deposited in the fracture and functions, inter alia, to hold the fracture open while maintaining channels through which produced fluids can flow upon completion of the fracturing treatment and release of the attendant hydraulic pressure.

An example of a well completion operation using a treating fluid containing particulates is gravel packing. Gravel packing treatments are used, inter alia, to reduce the migration of unconsolidated formation particulates into the well bore. In gravel packing operations, particles known in the art as gravel are carried to a well bore by a hydrocarbon or water carrier fluid. That is, the particulates are suspended in a carrier fluid, which may be viscosified, and the carrier fluid is pumped into a well bore in which the gravel pack is to be placed. The carrier fluid leaks off into the subterranean zone and/or is returned to the surface while the particulates are left in the zone. The resultant gravel pack acts as a filter to separate formation sands from produced fluids while permitting the produced fluids to flow into and through the well bore. Typically, gravel pack operations involve placing a gravel pack screen in the well bore and packing the surrounding annulus between the screen and the well bore with gravel designed to prevent the passage of formation sands through the pack. The gravel pack screen is generally a filter assembly used to support and retain the gravel placed during the gravel pack operation. A wide range of sizes and screen configurations are available to suit the characteristics of a well bore, the production fluid, and the subterranean formation sands. When installing the gravel pack, the gravel is carried to the formation in the form of a slurry by mixing the gravel with a viscosified carrier fluid. Once the gravel is placed in the well bore, the viscosity of the carrier fluid is reduced and it is returned to the surface. Such gravel packs are used to stabilize the formation while causing minimal impairment to well productivity. The gravel, inter alia, acts to prevent formation sands from occluding the screen or migrating with the produced fluids, and the screen, inter alia, acts to prevent the gravel from entering the well bore.

In some situations the processes of hydraulic fracturing and gravel packing are combined into a single treatment to provide a stimulated production and an annular gravel pack to reduce formation sand production. Such treatments are often referred to as “frac pack” operations. In some cases the treatments are completed with a gravel pack screen assembly in place with the hydraulic fracturing treatment being pumped through the annular space between the casing and screen. In this situation the hydraulic fracturing treatment ends in a screen out condition creating an annular gravel pack between the screen and casing. This allows both the hydraulic fracturing treatment and gravel pack to be placed in a single operation. In other cases the fracturing treatment may be performed prior to installing the screen and placing a gravel pack.

In order to prevent the subsequent flowback of proppant, gravel or other unconsolidated particulates with the produced fluids, a portion of the particulate introduced into the fractures or gravel packs may be coated with a hardenable resin composition. In the case of a fracturing operation, the fracture then closes on the proppant and applies pressure on the resin-coated particulates, causing the particles to be forced into contact with each other while the resin composition hardens. The hardening of the resin composition under pressure brings about the consolidation of the resin-coated proppant particles into a hard permeable mass having compressive and tensile strength meant to prevent unconsolidated particulates and formation sand from flowing out of the fractures with produced fluids. Flowback of formation sand with produced fluids is undesirable as it may erode metal equipment, plug piping and vessels, cause damage to valves, instruments, and other production equipment, and ultimately reduce the potential production of the well.

SUMMARY OF THE INVENTION

The present invention involves coated proppant slurries and using such slurries in subterranean applications such as production enhancement and sand control. More particularly, the present invention relates to stable resin-coated proppant suspensions that need not be immediately used once they are formed.

Some embodiments of the present invention provide methods of creating a stable slurry of coated particulates wherein the slurry is capable of being stored for at least 2 hours before use comprising the steps of: providing resin coated particulates wherein the resin comprises a resin that does not completely cure unless it is at least one of exposed to a temperature above about 175° F. or exposed to an external catalyst; and, substantially suspending the resin coated particulates in a servicing fluid to create a stable resin coated particulate slurry.

Other embodiments of the present invention provide methods of creating a stable slurry of coated particulates wherein the slurry is capable of being stored for at least 2 hours before use comprising the steps of: providing tackifier coated particulates; and, substantially suspending the tackifier coated particulates in a servicing fluid to create a tackifier coated particulate slurry.

The features and advantages of the present invention will be readily apparent to those skilled in the art upon a reading of the description of preferred embodiments that follows.

DESCRIPTION OF PREFERRED EMBODIMENTS

The present invention involves coated proppant slurries and using such slurries in subterranean applications such as production enhancement and sand control. More particularly, the present invention relates to stable resin-coated proppant suspensions that need not be immediately used once they are formed.

Some embodiments of the present invention describe methods of creating stable slurries of coated particulates comprising the steps of coating particulates with a resin or a tackifying compound and then substantially suspending the coated particulates in a servicing fluid to create a coated particulate slurry. Resins suitable for use in the present invention include those resins that do not fully cure until they are exposed to either temperatures above about 175° F. or an external catalyst. Tackifiers suitable for use in the present invention may be either used such that they form a non-hardening coating or they may be combined with a multifunctional material capable of reacting with the tackifying compound to form a hardened coating. The coated particulate slurries of the present invention are stable enough that they may be formed and used some time later. That is, the slurried particulates are retained in the fluidized state without significant settling during the period of time between when the slurry is made and when it is use in a subterranean operation.

The coated particulates of the present invention may be created in advance and, in the case of a resin or a hardened tackifyed coating, allowed to completely or partially cure or they may be coated directly before being substantially suspended in a servicing fluid.

Any high temperature curable resin that does not completely cure until exposed to temperatures above about 175° F. is suitable for use as a resin component in the present invention. When such resins are used, the resin on the particulate will not fully cure until it is placed in an environment, such as a subterranean formation, having a temperature of above about 175° F. Where the coated particulates slurries of the present invention are used in subterranean formations that are cooler than 175° F., an after-flush solution comprising an external catalyst may be applied to the coated particulates after they are placed in the subterranean formation. The use of an external catalyst to effect resin consolidation at reduced temperatures is known in the art, and it is within the ability of one skilled in the art, with the benefit of this disclosure, to select a suitable external catalyst based on the resin chosen and the subterranean conditions. Examples of suitable external catalysts include, but are not limited to, hydrochloric acid, phosphoric acid, acetic acid, fumaric acid, sulfonic acid, and combinations thereof. Examples of suitable external catalysts are hydrochloric acid, phosphoric acid, acetic acid, fumaric acid, sulfonic acid, and combination thereof.

Resins that do not completely cure until exposed to temperatures above about 175° F. are known in the art. Examples include, but are not limited to, furan-based resins, phenolic-based resins, and high-temperature (HT) epoxy-based resins. It is within the ability of one skilled in the art, with the benefit of this disclosure, to select a suitable resin.

Suitable furan-based resins include, but are not limited to, furfuryl alcohol resins, mixtures furfuryl alcohol resins and aldehydes, and a mixture of furan resins and phenolic resins. Of these, furfuryl alcohol resins are preferred. A furan-based resin may be combined with a solvent to control viscosity if desired. Suitable solvents for use with furan-based resins include, but are not limited to 2-butoxy ethanol, butyl acetate, and furfuryl acetate.

Suitable phenolic-based resins include, but are not limited to, terpolymers of phenol, phenolic formaldehyde resins, and a mixture of phenolic and furan resins. Of these, a mixture of phenolic and furan resins is preferred. A phenolic-based resin may be combined with a solvent to control viscosity if desired. Suitable solvents for use with phenolic-based resins include, but are not limited to, butyl acetate, butyl lactate, furfuryl acetate, and 2-butoxy ethanol.

Suitable HT epoxy-based resins include, but are not limited to, bisphenol A-epichlorohydrin resins, polyepoxide resins, novolac resins, glycidyl ethers and mixtures thereof. Of these, bisphenol A-epichlorohydrin resins are preferred. A HT epoxy-based resin may be combined with a solvent to control viscosity if desired. Suitable solvents for use with the HT epoxy-based resins of the present invention are those solvents capable of substantially dissolving the HT epoxy-resin chosen for use in the consolidation fluid. A co-solvent such as a dipropylene glycol methyl ether, dipropylene glycol dimethyl ether, dimethyl formamide, dimethyl sulfoxide, diethylene glycol methyl ether, ethylene glycol butyl ether, diethylene glycol butyl ether, propylene carbonate, d-limonene and fatty acid methyl esters, may also be used in combination with the solvent.

Resins suitable for use in the present invention may be combined with an optional hydrolyzable ester. When used, the hydrolyzable ester is generally included in the resin in an amount ranging from about 0.1 to about 3% by weight of the resin composition. Resin systems suitable for use in the present invention also may be combined with an optional silane coupling agent. Suitable silane coupling agents include, but are not limited to, n-2-(aminoethyl)-3-aminopropyltrimethoxysilane, 3-glycidoxypropyltrimethoxysilane, and n-beta-(aminoethyl)-gamma-aminopropyl trimethoxysilane. Where used, the silane coupling agent is generally included in the resin in an amount ranging from about 0.1% to about 3% by weight of the resin composition. Resin systems suitable for use in the present invention also may be combined with an optional surfactant. Suitable surfactants include, but are not limited to, an ethoxylated nonyl phenol phosphate ester, mixtures of one or more cationic surfactants, and one or more non-ionic surfactants with an alkyl phosphonate surfactant. Where used, the surfactant is generally included in the resin in an amount ranging from about 1% to about 15% by weight of the resin composition.

Compositions suitable for use as tackifying compounds in the present invention comprise any compound that, when in liquid form or in a solvent solution, will form a non-hardening coating upon a particulate. A particularly preferred group of tackifying compounds comprise polyamides that are liquids or in solution at the temperature of the subterranean formation such that they are, by themselves, non-hardening when introduced into the subterranean formation. A particularly preferred product is a condensation reaction product comprised of commercially available polyacids and a polyamine. Such commercial products include compounds such as mixtures of C₃₆ dibasic acids containing some trimer and higher oligomers and also small amounts of monomer acids that are reacted with polyamines. Other polyacids include trimer acids, synthetic acids produced from fatty acids, maleic anhydride and acrylic acid and the like. Such acid compounds are commercially available from companies such as Witco Corporation, Union Camp, Chemtall, and Emery Industries. The reaction products are available from, for example, Champion Technologies, Inc. and Witco Corporation. Additional compounds which may be used as tackifying compounds include liquids and solutions of, for example, polyesters, polycarbonates and polycarbamates, natural resins such as shellac and the like. Suitable tackifying compounds are described in U.S. Pat. No. 5,853,048 issued to Weaver, et al., U.S. Pat. No. 5,839,510 issued to Weaver, et al., and U.S. Pat. No. 5,833,000 issued to Weaver, et al., the relevant disclosures of which are herein incorporated by reference.

Tackyfiers suitable for use in the present invention may be either used such that they form non-hardening coating or they may be combined with a multifunctional material capable of reacting with the tackifying compound to form a hardened coating. A “hardened coating” as used herein means that the reaction of the tackifying compound with the multifunctional material will result in a substantially nonflowable reaction product that exhibits a higher compressive strength in a consolidated agglomerate than the tackifying compound alone with the particulates. In this instance, the tackifying compound also functions as the hardenable resin. Multifunctional materials suitable for use in the present invention include, but are not limited to, aldehydes such as formaldehyde, dialdehydes such as glutaraldehyde, hemiacetals or aldehyde releasing compounds, diacid halides, dihalides such as dichlorides and dibromides, polyacid anhydrides such as citric acid, epoxides, furfuraldehyde, glutaraldehyde or aldehyde condensates and the like, and combinations thereof. In some embodiments of the present invention, the multifunctional material may be admixed with the tackifying compound in an amount of from about 0.01 to about 50 percent by weight of the tackifying compound to effect formation of the reaction product. In some preferably embodiments, the compound is present in an amount of from about 0.5 to about 1 percent by weight of the tackifying compound. Suitable multifunctional materials are described in U.S. Pat. No. 5,839,510 issued to Weaver, et al., the relevant disclosure of which is herein incorporated by reference.

Particulates suitable for use in the present invention may be comprised of any material suitable for use in subterranean operations, including graded sand, bauxite, ceramic materials, glass materials, metal beads or balls, nut hulls, polymer beads, and the like. The particulate size generally may range from about 2 to about 400 on the U.S. Sieve Series, however, it is to be understood that in certain circumstances other sizes may be desired and will be entirely suitable for practice of the present invention. In some embodiments of the present invention, the particulate is graded sand having a particle size in the range of from about 10 to about 70 mesh, U.S. Sieve Series. It is within the ability of one skilled in the art, with the benefit of this disclosure, to select a suitable particulate composition and size.

The coated particulates of the present invention may be suspended in any servicing fluid known in the art, including aqueous gels, foams, emulsions, and viscosified fluids. Suitable aqueous gels are generally comprised of water and one or more gelling agents. The emulsions may be comprised of two or more immiscible liquids such as an aqueous gelled liquid and a liquefied, normally gaseous fluid, such as nitrogen. The preferred servicing fluids for use in accordance with this invention are aqueous gels comprised of water, a gelling agent for gelling the water and increasing its viscosity, and optionally, a cross-linking agent for cross-linking the gel and further increasing the viscosity of the fluid. The increased viscosity of the gelled or gelled and cross-linked servicing fluid, inter alia, reduces fluid loss and allows the fracturing fluid to transport significant quantities of suspended particulates. The servicing fluids may also include one or more of a variety of well-known additives such as breakers, stabilizers, fluid loss control additives, clay stabilizers, bactericides, and the like.

The slurries of the present invention may be created off-site from their location of final use and yet retain the ability to provide consolidation when used. In some embodiments of the present invention, the slurries may be created a few hours or a few weeks before they are used. A “stable” slurry of the present invention refers to a slurry in which the coated particulates are substantially slurried in the servicing and are retained in the fluidized state without significant settling during the period of time between when the slurry is made and when it is use in a subterranean operation. Moreover, in the stable slurries of the present invention the particulates retain their character as individual grains or small clusters, without forming large flocculations or aggregates. The stable slurries of the present invention are capable of being stored for 2 hours or longer after they are formed and before they are used in a subterranean operation.

Where it is desirable to store the slurry for a period of time longer than about a few hours, the viscoelastic properties of the servicing fluid must be controlled to ensure that the particulates remain suspended. U.S. Pat. No. 5,799,734, the relevant disclosure of which is herein incorporated by reference, describes such fluids and methods of their creation. Desirable viscoelastic properties of servicing fluids suitable for use in forming slurries that may be stored for more than a few hours without significant settling are: (1) apparent viscosity (at a shear rate of 1) from about 40,000 cp to about 200,000 cp; (2) Maxwellian Stress Relaxation of from about 1 to about 3 minutes; and (3) Maxwellian Equilibrium Limit from about 0.035 to about 0.1. In some embodiments of the present invention, the slurry may be diluted with a less viscous servicing fluid at the well site directly before use in the subterranean formation. In that way, the desirable viscoelastic properties help maintain the stability of the slurry after it is formed and yet a lower viscosity fluid can actually be used in the subterranean treatment.

Some embodiments of the methods of the present invention provide methods for creating stable slurries of coated particulates comprising the steps of coating a particulate with a resin or a tackifying compound and then substantially slurrying the coated particulates in a servicing fluid to create a coated particulate slurry.

Other embodiments of the present invention provide methods of propping a fractured subterranean formation comprising the steps of coating a particulate with a resin or a tackifying compound and then substantially suspending the coated particulates in a fracturing fluid to create a coated particulate slurry, and placing the coated particulate slurry into at least one fracture in the subterranean formation. Where the fracturing methods of the present invention are used on subterranean formations that exhibit a temperature of below about 175° F., and a resin coating is used, after the step of placing the resin coated particulate suspension into a fracture the method may further comprise the step of placing into the subterranean formation an after-flush solution comprising an external catalyst capable of causing the resin to cure.

Still other embodiments of the present invention provide methods of installing a gravel pack in a well bore comprising the steps of coating a particulate with a resin or a tackifying compound and then substantially suspending the coated particulates in a fracturing fluid to create a coated particulate slurry, and introducing the coated particulate slurry to the well bore such that the coated particulates form a gravel pack substantially adjacent to the well bore. Where the gravel packing methods of the present invention are used on well bores that exhibit a temperature of below about 175° F., and a resin coating is used, after the step of forming a gravel pack substantially adjacent to the well bore, the method may further comprise the step of placing an after-flush solution comprising an external catalyst into the subterranean formation.

To facilitate a better understanding of the present invention, the following examples of some of the preferred embodiments are given. In no way should such examples be read to limit the scope of the invention.

EXAMPLES Example 1

Both high-temperature epoxy resin and furan resin systems were evaluated to determine their suitability for use in as resin components of the present invention. For each resin system, a volume of 7.5 mL of resin was coated directly onto 250 grams of dry bauxite proppant. The resin-coated proppant was then mixed with 300 mL of 35 lbs/Mgal uncrosslinked carboxymethyl hydroxypropyl guar fracturing fluid. The suspension was then allowed to sit at approximately 74° F. for from 1 day to 14 days. Next, a zirconium crosslinker was added to the suspension and it was subjected to heating in the hot bath and stirring at 180° F. for 60 minutes to simulate the effect of pumping downhole and suspending in created fractures. After stirring period, the resin-treated proppant was packed into brass chamber and cured at 325° F. for 24 hours without applying any stresses. After curing, the consolidated cores were obtained for unconfined compressive strength measurements (Table 1).

TABLE 1 Unconfined Compressive Strengths (psi) Suspension time in gelled fluid at 74° F. Epoxy resin Furan resin  1 day 1265 1200  7 days 1390 825 14 days 930 1080

Table 1 illustrates that epoxy and furan resins are both suitable for use in the present invention, even where the mixtures were formed two weeks before use.

Therefore, the present invention is well adapted to carry out the objects and attain the ends and advantages mentioned as well as those that are inherent therein. While numerous changes may be made by those skilled in the art, such changes are encompassed within the spirit and scope of this invention as defined by the appended claims. 

1. A method of installing a gravel pack in a well bore comprising the steps of: providing resin coated particulates wherein the resin comprises a resin that does not completely cure unless it is at least one of: exposed to a temperature above about 175° F. or exposed to an external catalyst; providing a gravel packing fluid; substantially slurrying the resin coated particulates in the gravel packing fluid to create a resin coated particulate slurry wherein the slurry is capable of being stored for at least 2 hours before use; introducing the resin coated particulate mixture to the well bore such that the resin coated particulates form a gravel pack substantially adjacent to the well bore; and, allowing the resin coated particulates to substantially cure.
 2. The method of claim 1 wherein the high temperature curable resin is selected from the group consisting of a furan-based resin, a phenolic-based resin, a high-temperature (HT) epoxy-based resin, a phenol/phenol formaldehyde/furfuryl alcohol resin, and a combination thereof.
 3. The method of claim 1 wherein the high temperature curable resin further is selected from the group consisting of a hydrolyzable ester, a silane coupling agent, a surfactant, and a combination thereof.
 4. The method of claim 1 where in the external catalyst is selected from the group consisting of hydrochloric acid, phosphoric acid, acetic acid, fumaric acid, sulfonic acid, and combinations thereof.
 5. The method of claim 1 wherein the gravel packing fluid is selected from the group consisting of an aqueous gel, a foam, an emulsion, a crosslinked viscosified fluid, and a combination thereof.
 6. The method of claim 1 wherein the high temperature curable resin is coated onto the particulates on-the-fly.
 7. The method of claim 1 wherein the well bore exhibits a temperature at above about 175° F.
 8. The method of claim 1 wherein the subterranean formation exhibits a temperature of below about 175° F. and further comprising, after the step of introducing the resin coated particulate slurry to the well bore such that the resin coated particulates form a gravel pack substantially adjacent to the well bore, the step of placing an after-flush solution comprising an external catalyst into the well bore.
 9. The method of claim 1 wherein the gravel packing fluid has an apparent viscosity (at a shear rate of 1) from about 40,000 cp to about 200,000 cp; a maxwellian stress relaxation of from about 1 to about 3 minutes; and a maxwellian equilibrium limit from about 0.035 to about 0.1.
 10. A method of installing a gravel pack in a well bore comprising the steps of: providing tackifier coated particulates; providing a gravel packing fluid; substantially slurrying the tackifier coated particulates in the gravel packing fluid to create a tackifier coated particulate slurry wherein the slurry is capable of being stored for at least 2 hours before use; and, introducing the tackifier coated particulate slurry to the well bore such that the tackifier coated particulates form a gravel pack substantially adjacent to the well bore.
 11. The method of claim 10 wherein the tackifier is selected from the group consisting of a polyamide, a polyester, a polycarbonate, polycarbamate, a natural resin, and a combination thereof.
 12. The method of claim 10 wherein the gravel packing fluid is selected from the group consisting of an aqueous gel, a foam, an emulsion, a crosslinked viscosified fluid, and a combination thereof.
 13. The method of claim 10 wherein the tackifier is coated onto the particulates on-the-fly.
 14. The method of claim 10 further comprising the step of: combining the tackifier coated particulates with a multifunctional material before the step of: substantially suspending the tackifier coated particulates in a servicing fluid to create a tackifier coated particulate slurry wherein the slurry is capable of being stored for at least 2 hours before use.
 15. The method of claim 10 wherein the multifunctional material is selected from the group consisting of an aldehyde; a dialdehyde; a hemiacetal; an aldehyde releasing compound; a diacid halide; a dihalide; a polyacid anhydride; an epoxide; furfuraldehyde, glutaraldehyde or aldehyde condensates; and combinations thereof.
 16. The method of claim 10 wherein the gravel packing fluid has an apparent viscosity (at a shear rate of 1) from about 40,000 cp to about 200,000 cp; a maxwellian stress relaxation of from about 1 to about 3 minutes; and a maxwellian equilibrium limit from about 0.035 to about 0.1. 